Three differentacrylatemonomerscontainingacyclohexylmoietyweredesignedandsynthesizedto
preparetransparentacrylicpressuresensitiveadhesives(PSAs)comprisedofsemi-interpenetrated
structured polymernetworks.Theeffectsofsubstituentstructureintheacrylatemonomeronthe
adhesion performanceoftheacrylicPSAwereinvestigated.ThepreparedUV-curableacrylicPSAsyrups
werecharacterizedandtheopticalpropertiesoftheiracrylicPSA film werealsoexamined.Theacrylic
PSAs exhibitedhightransparencyinthevisiblewavelengthregion.Adhesionperformancewasevaluated
using thepeelstrength,cohesionstrength,andprobetacktests.Theadhesionpropertiesoftheacrylic
PSAs dependedonthesubstituentstructureintheacrylatemonomer